Heat Shrink Wrapper for Pipe Joint Heat Shrink Wrapperis anti-corrosion of pipeline,include the oil & gas steel pipeline and Metal Reinforced HDPE Corrugated pipeline etc.Say the area include oil & gas,waste water,drainage and sewage.
Heat Shrink Wrapper
Heat Shrink Wrapper which are devoloped and manufactured by Qingdao Huashida Plastic Co.,Ltd.major target is anti-corrosion of pipeline,include the oil & gas steel pipeline and Metal Reinforced HDPE Corrugated pipeline etc.Say the area include oil & gas,waste water,drainage and sewage.
( Our Company Heat shrinkable sleeve and heat shrinkable sleeve equipment can be provided)
THE HSS composed by radiation cross-linked polyethylene backing and high shearing strength adhesive .
It is mainly used for wrapping around pipe, anti-corrosion of kinds of pipe joints, and repairing pipes.
For example: Oil and gas pipe, inspection well and drainage pipe (Metal reinforced PE spiral pipe, hollow wall spiral pipe etc.), thermo insulated pipe, 3PE/2PE steel pipe.
Cathodic protection.External organic coatings for the corrosion protection of buried or immersed steel pipelines used in conjunction with cathodic protection.Tapes and Shrinkable materials.
External organic coatings for the corrosion protection of buried or immersed pipelinesfor continuous operating temperatures up to 50ºC-Tapes and Shrinkable materials.
Peel Strength Standard-Tapes and Shrinkable materials.
|NO||Text Item||Unit||Performance||Text Result||Text Method|
|1||Tensile Strength||MPa||≥17||19.47||ASTM D638|
|3||Vicat Softening Point||ºC||≥90||92||ASTM D1525|
|4||Brittleness Temperature||ºC||<-65||<-65||ASTM D2671C|
|5||Dielectric Strength||MV/m||≥25||33.13||ASTM D149|
|6||Volume Resistivity||Ω.m||≥1*1013||1.1*1013||ASTM D257|
|7||Environment Stress Crack||h||≥1000||>1000||GB/T1842|
|Chemical resistance (7d)||10% HCI||Tensile strength||MPa||≥85||104.9||ASTM D638|
|10% NaAH||Tensile strength||MPa||≥85||102.1||ASTM D638|
|10% NaCL||Tensile strength||MPa||≥85||108.3||ASTM D638|
|9||Thermal aging (150ºC,168h)||Tensile strength||MPa||≥14||20.7||ASTM D638|
|Text Item||Unit||Performance||Text Result||Text Method|
|Softening Point||ºC||≥90||90.1||ASTM E28|
|Brittleness Temperature||ºC||<-15||<-15||ASTM D2671C|
|Lap Shear||MPa||≥1.0||1.5||ASTM D1002|
|Steel N/cm||≥70||145.6||ASTM D1000|
|Primer N/cm||≥70||205.9||ASTM D1000|
|PE Layer N/cm||≥70||190.0||ASTM D1000|
NON-Solvent Epoxy Primer
|Text Item||Unit||Performance||Text Result||Text Menthod|
|Shear of cured perimer||MPa||≥5.0||12||SY/T0041|
Huashida Machinery, with over 14 years' experience, is one of the professional Heat Shrink Wrapper manufacturers in China. Offering the customized service, we warmly welcome you to get the high qualified products from our factory.